New Insights of Wear Behavior Analysis on Low Temperature Treated AISI 253MA Stainless steel Material by Gas Nitriding Process
Mechanical Engineering Department, Gokaraju Rangaraju Institute of Engineering & Technology, Hyderabad, India
* Corresponding author: ramyasreekeerthi@gmail.com
AISI 253MA Stainless steel samples were treat with the gas nitrating process at low heat around 450°C. It was seen that all-inclusive austenite stage exist when it is nitrade to 8 hours and post addition at time of nitrading to 16 hours the mix of ferrites and progressively substance of nitrogen was gathered in the following layers. Farther nitrading to 24 hour it has seen at Cr-N stage was discovered and turns the steel progressively firmer superficially. Erode tests were led by tribological wear testing machine to examine the tribological wear loss. Volume wear was found to be least in 18 hours test which demonstrated better improvement of wear improvement. High hardness were found in 24 hrs showing a hardness of 1080Hv. The sample nitrided to 24 hours exhibited better wear resistance, high hardness and low wear loss as well as low volume wear loss. Assessment examinations of nitrided test samples were investigated under scanning electron magnifying analysis.
© The Authors, published by EDP Sciences, 2020
This is an Open Access article distributed under the terms of the Creative Commons Attribution License 4.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.