Influence of silane on the structure of polystyrene prepared by sol-gel coatings via UV curing
Bilecik Seyh Edebali University, Vocational School. Department of Chemical Technologies, 11030 BİLECİK, Turkey
2 Bilecik Seyh Edebali University, Faculty of Engineering, Department of Chemistry and Process Engineering, 11030 BİLECİK, Turkey
* Corresponding author: email@example.com
Light, heat, oxygen, moisture, ozone, atmospheric pollution and biological effects are the most important effectives wreak to chemical degradation in the polymer structure. In result of chemical degradation on the polymer consist of problems such as discoloration, brittleness, surface cracks, perspiration, crumbling, smell, surface acidity. In this work, it is aimed to improve the problem of the polystyrene (PS) material against chemical degradation. For this reason, PS is coated with silica sol-gel hybrid coating. Silica sol-gel was synthesized by using vinyltrimethoxysilane (VTMS) as a cross-linker and tetraethylorthosilicate (TEOS) as a silica source. Firstly, four different pre-treatment technique (oven, vacuum oven, lyophilizer and freezing) was studied to determine the most suitable pre-treatment technique for coating on PS substrate of sol-gel prepared with initial formulation (S1). A freezing technique gave the best results for coating sample. The change of surface colour of coated PS was measured by CIE L*a*b* methods. Secondly, the most suitable curing agent (Irgacure 184, Irgacure 819, Darocur 1173 and TiO2 as crystalline anatase phase) was determined to coat the sol-gel on PS. It was determined to the lowest yellowing of PS surface hybrid coated as UV curing of TEOS sol modified by VTMS and TiO2 as photo-initiators. Finally, the chemical and morphological structure of the coated PS samples was determined by FT-IR and SEM instruments, respectively.
© The Authors, published by EDP Sciences, 2017
This is an Open Access article distributed under the terms of the Creative Commons Attribution License 4.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited. (http://creativecommons.org/licenses/by/4.0/).
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.