- Xu Xian, Wu Guozhong, Bao Yanrong, et al. Analysis on fracture fault of aluminum device clamp in substation[J]. Casting Forging Welding, 2012, 41(7): 191-195. [Google Scholar]
- Dong Jin, Zhong Xiangyuan, An Yinghong. Fracture of copper and aluminum middle-sized device clamp in substation[J]. Electric Power, 2010, 43(12):27-30. [Google Scholar]
- Hong Yicheng, Cai Jianbin. Analysis on fracture reasons of rectangular hanging plates of hanging fittings in the 220 kV electric transmission line[J]. PTCA (PART A :PHYSTEST), 2017, 53(5): 361-364. [Google Scholar]
- Cause of cracking on power grid terminal connector[J]. PTCA (PART A :PHYSTEST), 2021, 51(7): 66-73. [Google Scholar]
- Xia Xiaojian, Zhang Konglin, Lin Deyuan. Failure analysis on cracking of an aluminum alloy flangefor current transformer[J]. PTCA (PART A :PHYSTEST), 2017, 53(10): 754-760. [Google Scholar]
- Dong Zhongli, Hu Ping, Luo Xue. Fracture failure analysis on cast aluminum alloy splint of highvoltage isolation switch static contact[J]. Mechanical and Electrical Engineering Technology, 2017, 46(2): 76-78. [Google Scholar]
- Wang Ruoming, Zhan Maji, Ji Kun, et al. Failure reason of tension clamp for high voltage electricity transmission[J]. Materials for Mechanical Engineering, 2017, 41(3): 112-116. [CrossRef] [Google Scholar]
- Xu Xuexia, Ouyang Jie, Feng Yanting, et al. Analysis on crack failure of terminal connector[J]. Casting Forging Welding, 2011, 40(13): 160-163. [Google Scholar]
- Xu Jie. Reasons and improvement measures for 110 kV equipment wire clamps[J]. Yunnan Electrical Power, 2006, 34(3): 45. [Google Scholar]
- Luo Hong Jian, Gong Zhuo, Wang Jionggeng, et al. Failure analysis of aluminum terminal connector[J]. Journal of Yunnan Normal University Journal, 2018, 38(5): 44-48. [Google Scholar]
- DL/T 1785-2017. Directive for X-ray digitalradiography of electric power equipment[S]. National Energy Administration, 2018. [Google Scholar]
- GB/T 13298-2015. Inspection methods of microstructure for metals[S]. General Administration of Quality Supervision, Inspection and Quarantine of the People’s Republic of China, 2016. [Google Scholar]
- JY/T 010-1996. General rules for analytical scanning electron microscopy[S]. State Education Commission, 1997. [Google Scholar]
- Ding Wenbin, Fang Wen, Zhang Chaolei, et al. Failure analysis of double conductor aluminum equipment wire clamp for transmission tower[J]. Special Casting Nonferrous Alloys, 2023, 43(3): 359-362. [Google Scholar]
- Luo Changsen, Luo Hong, Zeng Xianguang. Fracture analysis of Al alloy ZL102 polishing machine ring[J]. Special Casting Nonferrous Alloys, 2013, 33(3): 285-288. [Google Scholar]
- Han Jiceng, He Jian, Lin Deyuan. Fracture reason of L-type junction board of capacitor voltage transformer accessory in a substation[J]. Materials for Mechanical Engineering, 2020, 44(7): 98-102. [Google Scholar]
- GB/T1173-1995. Casting aluminium alloys[S]. The State Bureau of Quality and Technical Supervision, 1996. [Google Scholar]
- Q/GDW11717-2017. Technical supervision code for metal in power grid equipment[S]. State Grid Corporation of China, 2018. [Google Scholar]
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.