Mechanical adhesion energy of thermal oxide scale on 0.01 and 0.12 wt.% Si-containing hot-rolled steels

Open Access

Issue		E3S Web Conf. Volume 602, 2025 International Conference on Materials and Energy (ICOME2024)


Article Number		02001
Number of page(s)		4
Section		Materials
DOI		https://doi.org/10.1051/e3sconf/202560202001
Published online		14 January 2025

R. Lu, G. Wu, J. Zhang, Effect of carbon on isothermal reduction of high-strength steel oxide scale in 30% H₂–N₂ atmosphere. J. Clean. Prod. 279, 123681 (2021). [CrossRef] [Google Scholar]
Q. Yuan, G. Xu, M. Zhou, B. He, The effect of the Si content on the morphology and amount of Fe₂SiO4 in low carbon steels. Met. 6.4, 94 (2016). [Google Scholar]
J. Liu, G. Jiang, Use of laboratory indentation tests to study the surface crack propagation caused by various indenters. Eng. Fract. Mech. 241, 107421 (2021). [CrossRef] [Google Scholar]
M. M. Islam, S. I. Shakil, N. M. Shaheen, P. Bayati, M. Haghshenas, An overview of microscale indentation fatigue: Composites, thin films, coatings, and ceramics. Micron. 148, 103110 (2021). [CrossRef] [PubMed] [Google Scholar]
H. Xin, R. Borduin, W. Jiang, K. M. Liechti, W. Li, Adhesion energy of as-grown graphene on copper foil with a blister test. Carbon. 123, 243–249 (2017). [CrossRef] [Google Scholar]
J. D. Hübsch, P. L. Rosendahl, C. Mittelstedt, Blister tests on thin-walled composite structures at different temperatures. Int. J. Adhes. Adhes. 110, 102907 (2021). [CrossRef] [Google Scholar]
Y. Kondo, H. Tanei, Adhesive strength of oxide scale formed on low-carbon steel. Jpn. Soc. Technol. Plast. 54.634, 984–987 (2013). [CrossRef] [Google Scholar]
C. Pascal, M. Braccini, V. Parry, E. Fedorova, M. Mantel, D. Oquab, D. Monceau, Relation between microstructure induced by oxidation and roomtemperature mechanical properties of the thermally grown oxide scales on austenitic stainless steels. Mater. Charact. 127, 161–170 (2017). [CrossRef] [Google Scholar]
H. E. Evans, Predicting oxide spallation from sulphur contaminated oxide/metal interfaces. Oxid. Met. 79.1, 3–14 (2013). [CrossRef] [Google Scholar]
F. Toscan, L. Antoni, Y. Wouters, M. Dupeux, A. Galerie, Oxidation kinetics and scale spallation of iron-chromium alloys with different titanium contents. Mater. Sci. Forum. 461, 705–712 (2004). [CrossRef] [Google Scholar]
Y.-L. Yang, C.-H. Yang, S.-N. Lin, C.-H. Chen, W.-T Tsai, Effects of Si and its content on the scale formation on hot-rolled steel strips. Mater. Chemist. Phys. 112, 566–571 (2008). [CrossRef] [Google Scholar]

Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.

Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.

Initial download of the metrics may take a while.