Controllable Preparation and the Tribological Properties of Bimetal Oxide ZnxTiyOz
College of Mechanical and Electrical Engineering, Shaanxi University of Science and Technology, Xi’an 710021, PR China
* The corresponding author’s e-mail address: 1805029@sust.edu.cn
The bimetallic oxide films with different contents of Zn and Ti were prepared by magnetron sputtering and the films were annealed at 600°C. The relationship between the structure and properties with different content of elements before and after annealed was comprehensively analyzed. It was found that with the decrease of Zn content, the number of the nuclear inside the film increased and the surface became denser. Therefore, the hardness and bonding strength gradually increased. The friction coefficient and the wear rate of the film were 0.154 and 7.4×10-6 mm3/N/m respectively, due to the formation of ZnTiO3 and ZnO composite phases with lubricity on the surface.
© The Authors, published by EDP Sciences, 2020
This is an Open Access article distributed under the terms of the Creative Commons Attribution License 4.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.